Part II: Oxidative Thermal Aging of Pd/Al2O3 and Pd/CexOy-ZrO2 in Automotive Three Way Catalysts: The Effects of Fuel Shutoff and Attempted Fuel Rich Regeneration

Zheng, Qinghe; Farrauto, Robert; Deeba, Michel

The Pd component in the automotive three way catalyst (TWC) experiences deactivation during fuel shutoff, a process employed by automobile companies for enhancing fuel economy when the vehicle is coasting downhill. The process exposes the TWC to a severe oxidative aging environment with the flow of hot (800 °C–1050 °C) air. Simulated fuel shutoff aging at 1050 °C leads to Pd metal sintering, the main cause of irreversible deactivation of 3% Pd/Al2O3 and 3% Pd/CexOy-ZrO2 (CZO) as model catalysts. The effect on the Rh component was presented in our companion paper Part I. Moderate support sintering and Pd-CexOy interactions were also experienced upon aging, but had a minimal effect on the catalyst activity losses. Cooling in air, following aging, was not able to reverse the metallic Pd sintering by re-dispersing to PdO. Unlike the aged Rh-TWCs (Part I), reduction via in situ steam reforming (SR) of exhaust HCs was not effective in reversing the deactivation of aged Pd/Al2O3, but did show a slight recovery of the Pd activity when CZO was the carrier. The Pd+/Pd0 and Ce3+/Ce4+ couples in Pd/CZO are reported to promote the catalytic SR by improving the redox efficiency during the regeneration, while no such promoting effect was observed for Pd/Al2O3. A suggestion is made for improving the catalyst performance.


Also Published In

More About This Work

Academic Units
Earth and Environmental Engineering
Published Here
February 15, 2016
Academic Commons provides global access to research and scholarship produced at Columbia University, Barnard College, Teachers College, Union Theological Seminary and Jewish Theological Seminary. Academic Commons is managed by the Columbia University Libraries.